Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
Oral Health and Preventive Dentistry
Login:
Benutzername:

Kennwort:

Plattform:

Kennwort vergessen?

Registrieren

Oral Health Prev Dent 18 (2020), Nr. 3     8. Juni 2020
Oral Health Prev Dent 18 (2020), Nr. 3  (08.06.2020)

Open Access ORAL MEDICINE, Online Article, Seite 529-536, doi:10.3290/j.ohpd.a44689, PubMed:32515424, Sprache: Englisch


Online Article: Quantitative and Qualitative Evaluation of Enamel Erosion Following Air Abrasion with Bioactive Glass 45S5
Dionysopoulos, Dimitrios / Tolidis, Kosmas / Tsitrou, Effrosyni / Kouros, Pantelis / Naka, Olga
Purpose: To evaluate the effect of pre-treatment air abrasion of surfaces using bioactive glass 45S5 on the progression of erosion in bovine enamel induced by a common soft drink.
Materials and Methods: Twelve intact bovine incisors were selected and 24 enamel samples were prepared and randomly assigned to two groups (n = 12): 1. control group, no anti-erosive treatment; 2. experimental group: samples were air abraded with bioglass 45S5 before the erosive challenge. The enamel samples were submitted to erosive cycling using a common soft drink. Enamel surface loss was evaluated using optical profilometry; surface microhardness and roughness changes were determined using Vickers method and Vertical Scanning Interferometry, respectively. In addition, SEM observations and EDS analysis were performed to detect any alterations in surface morphology and mineral content. The data were statistically analysed using one-way ANOVA and Tukey's post-hoc test at a significance level of α = 0.05.
Results: The experimental group exhibited less (18.7%) surface loss than did the control group (p < 0.05), while also presenting a statistically significantly smaller decrease in surface microhardness compared to the control group after erosive cycling (p < 0.05). However, neither group showed a statistically significant change in surface roughness (p > 0.05). After the treatments, changes in surface morphology and mineral content of enamel were observed.
Conclusions: Surface pre-treatment using air abrasion bioglass 45S5 may help prevent enamel erosion induced by excessive consumption of soft drinks. Further clinical trials are needed to confirm the effectiveness of this method and its clinical significance.

Schlagwörter: air abrasion, bioglass, enamel erosion, scanning electron microscopy, surface loss