Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
Oral Health and Preventive Dentistry
Login:
Benutzername:

Kennwort:

Plattform:

Kennwort vergessen?

Registrieren

Oral Health Prev Dent 8 (2010), Nr. 1     1. Apr. 2010
Oral Health Prev Dent 8 (2010), Nr. 1  (01.04.2010)

Seite 41-45, doi:10.3290/j.ohpd.a18825, PubMed:20480053, Sprache: Englisch


The Erosive Potential of 1% Citric Acid Supplemented by Different Minerals: An In Vitro Study
Magalhaes, Ana Carolina / Moraes, Samanta Mascarenhas / Rios, Daniela / Wiegand, Annette / Buzalaf, Marília Afonso Rabelo
Purpose: The objective of the present in vitro study was to evaluate the effect of different minerals in combination with 1% citric acid on dental erosion.
Materials and Methods: Ninety enamel samples were randomly allocated to nine groups (G1: pure 1% citric acid solution [control]; G2: with 1 mM Ca; G3: with 0.047 mM F; G4: with 1 mM Fe; G5: with 1 mM P; G6: with 1 mM Ca and 0.047 mM F; G7: with 1 mM Ca and 1 mM P; G8: with 1 mM Fe and 0.047 mM F; G9: with 1 mM Ca, 1 mM P, 0.047 mM F and 1.0 mM Fe). The samples were subjected to six pH cycles, each consisting of immersion in pure or modified 1% citric acid (1 min) followed by storage in artificial saliva (59 min). Enamel wear was assessed using profilometry.
Results: Data were analysed using analysis of variance and Tukey test (P < 0.05). Enamel loss (mean ± SD) amounted to between 0.87 ± 0.30 and 1.74 ± 0.74 lm but did not significantly differ among the groups.
Conclusions: The modification of 1% citric acid with different minerals did not have a protective effect on enamel erosion.

Schlagwörter: dental erosion, enamel, wear